Use of the electrochemical potential to characterise the surface damage behaviour of cyclically stressed materials
Within the scope of the research project, a corrosion measuring station is to be set up and integrated into a fatigue testing system so that electrochemical investigations can be carried out. By exposing the materials to various co
Use of the electrochemical potential to characterise the surface damage behaviour of cyclically stressed materials
Within the scope of the research project, a corrosion measuring station is to be set up and integrated into a fatigue testing system so that electrochemical investigations can be carried out. By exposing the materials to various corro
Within the investigations on the unalloyed and low-alloyed carbon steels C22R (SAE 1023) and 20MnCrS5 (SAE 5120), the magnetic property-stress-microstructure relationship is to be developed and made usable for the evaluation by means of magnetic measuring procedures. The two materials intended for the investigations have comparable chemical compo
back
Use of µmagnetic test methods for the evaluation of the damage evolution in metallic materials subjected to cyclic loading
In order to achieve the goal of a (residual) fatigue life calculation for metallic materials or structures, it is necessary that comprehensive information is determined and made available. This information descri
Use of µmagnetic test methods for the evaluation of the damage evolution in metallic materials subjected to cyclic loading
In order to achieve the goal of a (residual) fatigue life calculation for metallic materials or structures, it is necessary that comprehensive information is determined and made available. This information describes the micr
The S-N curve generated using accelerated lifetime prediction methods are based on only a few real data points due to the significantly reduced experimental effort. However, the database can be significantly expanded by generating virtual data points, which makes it possible to integrate statistical methods (Point 1).
In order to describe the s
Initial results on the integration of statistical methods into accelerated lifetime prediction using the example of the material C45E were presented at the conference “Steel Innovation” in April 2025. The procedure for generating an S-N curve with density function, to describe the scatter band, is shown and described below.
Utilisation of statistical approaches within the scope of lifetime prediction methods for notched specimens using the example of unalloyed steels
The construction of dynamically loaded metallic materials and components is usually based on the relation between the stress amplitude and the number of cycles to failure, which is displayed in S-N cu
Utilisation of statistical approaches within the scope of lifetime prediction methods for notched specimens using the example of unalloyed steels
The construction of dynamically loaded metallic materials and components is usually based on the relation between the stress amplitude and the number of cycles to failure, which is displayed in S-N curve